| Tempat asal | Cina |
| Nama merek | JT-RESIN |
| Sertifikasi | SGS，CE,UL |
| Nomor model | CASTING IMPREGNATION EPOXY RESIN UNTUK TRANSFORMER TIPE KERING KELAS F |
Resin Epoxy Cair Dan Hardner Potting Komposisi Casting Untuk Transformer Isolasi CT PT VT MV
Proporsi:
|
||
|
|
Aplikasi:
Untuk transformer dalam ruangan tegangan menengah dan tinggi,isolator listrik, seperti saklar dan bagian listrik, dll.
Metode pengolahan:
Pengeboran gravitasi diri vakum konvensional
Data produkNilai pedoman)*
JT 8068-1 A Resin epoksi modifikasi bebas cairan dan pelarut
| Nilai TIPIK* |
|
Viskositas @ 25°C, mPa.s [ISO 12058] 1500-3,000 Nilai epoksi, equiv/g [ISO 3001]........................................................................................................... (Bagian lain dari bahan kimia yang digunakan dalam pembuatan bahan kimia)0.45-0.51 Densitas @ 25°C, g/cm3[ISO 1675]...1.13-1.15 Tekanan uap @20°C, pa (knudsen)....<0.01 @60°C, pa ((knudsen)........................................................................................................................................................................................................................................... <0.5 Waktu penyimpanan @ 25°C (kapasitas kontainer tertutup), bulan...........................................12 |
Catatan:Untuk mencegah penyerapan kelembaban,sila simpan resin epoksi dalam wadah tertutup dan simpan pada suhu normal (sekitar 20 sampai 25 °C).
JT 8068-1 B Pengeras Epoxy cair yang dimodifikasi
| Nilai TIPIK* |
|
Viskositas @ 25°C, mPa.s [ISO 12058] Tekanan uap @ 20°C, mbar ((Knudsen)................................ (mengacu pada aturan yang berlaku).....................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................0.5 @ 60°C,mbar(Knudsen)................................................................................................... Ca.10 Densitas @ 25°C, g/cm3[ISO 1675]................................................................................................................................................................... (Selengkapnya tentang ISO 1675 dan ISO 1675), dan juga untuk pembagian data yang diperlukan untuk pembagian data tersebut.1.19-1.22 Waktu penyimpanan @ 25°C (kapasitas kontainer tertutup), bulan...........................................12 |
PerhatikanSetelah dipanaskan hingga 60°C, kristal dapat
harus dihilangkan; JT8068-1B berisi akselerator.Penyimpanan yang berkepanjangan pada suhu lingkungan yang tinggi akan mengakibatkan peningkatan viskositas yang tidak diinginkan dan melemahkan reaktivitas sistem resin casting.
Viskositas proses:
Daerah aplikasi: